SAE_J434-2004汽车球墨铸铁（中英文版）.pdf

SAE J434 Revised FEB2004 1 范围 该 SAE 标准涵盖了应用于汽车球墨铸铁铸件和相关的行业的铸铁试件的金相组织和最低 机械性能要求。铸件需详细说明是铸态或热处理状态。如果铸件需热处理，需获得客户的批 准。 本附录提供了在化学成分，显微组织和力学性能，铸造性能等方面面信息以及为特定条件 服务的其他信息。 在此标准的 SI 单位是磅 2. 2 参考文献 2.1 相关出版物 The following publications form a part of the specification to the extent specified herein. Unless otherwise indicated, the latest revision of SAE publications shall apply 2.1.1 ASTM 国际出版物 Available from ASTM INTERNATIONAL, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959 ASTM E10 –-Standard Test Method for Brinell Hardness of Metallic Materials ASTM E23—Standard Test Methods for Notched Bar Impact Testing of Metallic Materials ASTM E111—Standard Test Method for Young's Modulus, Tangent Modulus and Chord Modulus ASTM A247—Standard Test Method for Evaluation the Microstructure of Graphite in Iron Castings ASTM A536—Standard Specification for Ductile Iron Castings STP-455—Gray, Ductile, and Malleable Iron Castings Current Capabilities (out-of-print) 2.1.2 其他出版物 Metals Handbook, Vol. 1, 2, and 5, 8th Edition, American Society for Metals, Metals Park, OH Gray and Ductile Iron Castings Handbook, Gray and Ductile Iron Founder Society, Cleveland, OH H. D. Angus, Physical Engineering Properties of Cast Iron, British Cast Iron Research Association, Birmingham, England 3. 3 牌号 机械性能和冶金描述如表 1 所示。 级别 一般硬度范 描述 试样厚度 拉伸强度 屈服强度 延长率 围 （Mpa ） mm Mpa Ksi Mpa ksi % D400 143~170HBW 铁素体 ≤20 400 58 275 40 18 或商议而定 20<-≤40 260 40<-≤60 250 D450 156~217HBW 铁素体-珠光体 ≤20 450